high alumina cement

high alumina cement The goods has excellent high-temerperature Good anti-corrosion performance CA-50.60.70.75,80

high alumina Cement

Aluminate cement products for the alumina content of 50% -60% of the cement matrix.

Aluminate cement CA-50 series products, the main mineral phase composition of CA-phase (a calcium aluminum acid. 2 aluminum acid a calcium). Therefore, not only products with a relatively high temperature use of performance, but at the same time have a reasonable and stable hydration of the performance, rapid growth in outstanding physical strength properties 

The company's production of aluminate cement CA-50 series based on the development of cement hydration and the relative intensity of the physical strength to be the value of the product into different grades, so that customers according to their demand for the product and the use of conditions to choose. Meanwhile, through the production process of the optimization of product performance so that it can adapt to both the monolithic refractories different construction methods (such as: casting, injection), also can meet a variety of castable formula system, such as: the traditional combination of high alumina cement castables and medium-cement castables, the performance of the construction made by the different requirements.

This series of product does not contain any additives to ensure product suitability and stability.

Transport and storage:

 aluminate cement in the transport and storage process, special attention should be moisture-proof, to extend the storage period, to avoid affecting performance 

aluminate cement in the transport, storage and use of the process, to avoid cement and other species (such as the Portland cement, etc.) and harmful impurities (such as lime, etc.) contact;

 aluminate cement in the use of the process, mixing water should be pure, to avoid possible harmful impurities affect product performance

Performance indicators

This standard applies to my company's A500.A600.A700.A900 and CA50 series of aluminate cement products.

Chemical Composition

Detection index		CA-500,GB201-2000	A500	A600	A700	A900	CA-80
Al2O3	%	>=50.<60	>=50.<60			>=52.<60	>=77
SiO2		<=8.0	<=8.0			<=6.0	<=0.5
Fe2O3		<=2.5	<=2.5			<=2.5	<=0.5
R2O		<=0.4	<=0.4			<=0.4	<=0.4
S		<=0.1	-			--	--
Cl		<=0.1	-			-	--

Physical Property

Detection index		CA-50	A500	A600			A700			A900	CA-80
Fineness
0.045mm Sieve	%	<=20	-							<20	<=20
Bo's surface area	m2/kg	>=300	>=300							>=400	>=400
Setting time
Initial setting time	h:min	>=0:30	>=0:30							>=1:00	>=0:30
Final setting time		<=6:00	<=6:00							<=6:00	,=6:00
Flexural Level
1d	MPa	>=5.5	>=5.5			>=6.0			>=6.5	>=7.0	>=4.0
3d		>=6.5	>=6.5			>=7.0			>=7.5	>=9.0	>=5.0
Pressure Level
1d	MPa	>=40	>=40		>=45			>=52		>=72	>=25
3d		>=50	>=50		>=55			>=62		>=82	>=30